Abstract
The present study is aimed at investigating the hydraulic characteristics of ladle furnace slag (LFS), under the pretence of using LFS as a cement substitute in certain applications. Furthermore, LFS has been considered as a possible activator in a blend containing 50% LFS, and 50% ground granulated blast furnace slag (GGBFS). Phases detected in LFS were quantified using Rietveld analysis. Calorimetric studies were performed at 20, 25 and 30 °C in order to calculate the apparent activation energy of hydration and thereby to suggest a kinetic model for the tested compositions within this temperature interval. In addition, compressive strength tests were performed on mortar prisms made with LFS, and LFS/GGBFS which had hydrated for 2, 7 and 28 days. Both compositions reached acceptable early strengths, (e.g. LFS, 33.1 MPa, and LFS/GGBFS, 17.9 MPa, after 2 days), but after 28 days hydration the blend was superior to neat LFS. Related apparent activation energies were determined using an Avrami–Erofeev model and gave E a = 58 kJ/mol for neat LFS and E a = 63 kJ/mol for the blend. The results imply that LFS or a LFS/GGBFS blend can be favourably used as supplement in binder applications such as binder in by-product metallurgical briquettes, which are used as recycle to the blast furnace or basic oxygen furnace depending on the specific briquette composition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.