The influence of inoculant additions on the cooling curve characteristics, microstructure and chill depth of hypoeutectic grey cast iron melts treated with FeSi or SiC as silicon carriers has been investigated. The effect of SiC content, when used simultaneously with FeSi as a silicon carrier, on the solidification behaviour of melts with an identical carbon equivalent has also been studied. It has been found that the addition of SiC instead of FeSi as a silicon carrier resulted in variations in the thermal analysis characteristics and microstructure together with decreasing chill depth. These effects were more pronounced for inoculated melts. It was also observed that the maximum amount of A-type graphite, the finest microstructure and the minimum chill depth were obtained with 1.6–2.0 wt-%SiC additions, for grey cast iron melts (treated with SiC and FeSi) having carbon equivalents of 4.2%.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.