Abstract
The present work describes the processing of alumina fiber reinforced alumina ceramic preforms consisting of chopped Al 2O 3 fibers (33 wt%) and Al 2O 3 (67 wt%) fine powders by slip casting. The preforms were pre-sintered in air at 1100 °C for 1 h. A lanthanum based glass was infiltrated into these preforms at 1250 °C for 90 min. Linear shrinkage (%) was studied before and after glass infiltration. Pre-sintered and infiltrated specimens were characterized by scanning electron microscopy, energy dispersive X-ray, X-ray diffraction, porosimetry and flexural strength. The alumina preforms showed a narrow pore size distribution with an average pore size of ∼50 nm. It was observed that introducing Al 2O 3 fibers into Al 2O 3 particulate matrix produced warp free preforms with minor shrinkage during pre-sintering and glass infiltration. It was observed that the infiltration process fills up the pores and considerably improves the strength and reliability of alumina preform.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.