Abstract
An Ag nanoparticle sintering is a promising die attach method for use in high-temperature electronics and could potentially be substituted for conventional high Pb-containing solders. An electroless Ni/immersion Au (ENIG) is a common surface finish for solder, wire bonding, and Ag nanoparticle sintering. However, there is no report on the influence of ENIG defects on the shear strength and bonding quality of Ag nanoparticle sintered joint. In this study, the relationship between the presence of ENIG defects and shear strength of Ag nanoparticle sintered joint after bonding and isothermal aging test using two types of ENIG surface finished Cu substrates (with ENIG defects and without defects) was investigated. The initial shear strength of Ag sintered joint showed similar values of approximately 36 MPa despite the presence of ENIG defects. However, the ENIG defects could affect the shear strength degradation of Ag sintered joint after thermal aging at 250 °C. This degradation came from the Ni oxidation by the presence of ENIG defects and subsequent brittle fracture of joint alone the Ni oxidation layer.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.