Abstract
BackgroundDeveloping efficient bonding techniques for orthodontic brackets and all-ceramic materials continues to pose a clinical difficulty. This study aimed to evaluate the shear bond strengths (SBS) of metal and ceramic brackets to various all-ceramic CAD-CAM materials, such as lithium disilicate CAD (LDS-CAD), polymer-infiltrated ceramic (PIC), zirconia-reinforced lithium silicate glass ceramic (ZLS), and 5YTZP zirconia after different surface treatments and thermal cycling.Materials and methodsThe samples were divided into two groups to be bonded with ceramic and metal lower incisor brackets. Each group was subdivided into a control group devoid of any surface treatment, 10% HF acid (HFA) etching, ceramic etch & prime (MEP), Al2O3 air abrasion, and medium grit diamond bur roughening. After surface treatment, brackets were bonded with composite resin cement, thermal cycled, and tested for shear bond strength. The failed surfaces were evaluated with a digital microscope to analyse the type of failure. The data were statistically analysed using a one-way ANOVA and Tukey HSD tests at p < 0.05.ResultsThe highest mean bond strengths were found with HFA etching in LDS-CAD (13.17 ± 0.26 MPa) and ZLS (12.85 0.52 MPa). Diamond bur recorded the lowest mean bond strength roughening across all the ceramic groups. There were significant differences in mean shear bond values per surface treatment (p < 0.001) and ceramic materials.ConclusionAmong the surface treatment protocols evaluated, HFA etching and MEP surface treatment resulted in enhanced bond strength of both ceramic and metal brackets to CAD-CAM all ceramic materials.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.