Abstract
The water–silica fume–cement system is highly sensitive to the effect of superplasticizers. This work aimed to study the individual effects of the dosage and delayed addition time of laboratory synthesized sodium sulfanilate phenol formaldehyde condensate (SSFP) on the hydration characteristics of sulfate resisting cement (SRC) pastes incorporating 10mass% SF and hydrated up to 90days. Initial and final setting times, compressive strength, bulk density, total porosity and hydration kinetics were determined. Some selected specimens were analyzed using IR spectroscopy. The results showed that the fluidity of cement pastes increases with SSFP dosage and delayed addition time up to 10min this is due to the electrostatic repulsion between cement particles and the decrease of C3A content that is minimized by hydration until the dormant period (10–15min). The values of combined water, compressive strength and bulk density increase with polymer content up to 1.5mass% with delayed addition time up to 10min; this is intrinsically associated with the reduction of W/C ratio with polymer content as well as the improvement of superplasticizing effect of SSFP with delayed addition. IR spectra are in a good agreement with the results of physico-chemical and mechanical properties. The synthesized SSFP condensate could improve the fluidity, bulk density and compressive strength of the investigated cement pastes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have