Abstract

Mechanical properties of SiO2-Al2O3 ceramics were studied in relation to the chemical composition. Raw powders of the composition ranging from 60 to 78wt% Al2O3 were synthesized by the spray pyrolysis method and sintered at 1650°C for 4h. The room temperature flexural strength and fracture toughness of the specimens showed no significant difference with the composition ranging from 66 to 78wt% Al2O3. But for the SiO2-rich specimens containing less than 66wt% Al2O3, those values decreased slightly. For the Al2O3-rich specimens which contain no glassy phase, the high-temperature strength and fracture toughness decreased gradually with increasing temperature. In contrast, the strength and the KIC of the specimens containing both mullite and a glassy phases increased with increasing silica content and increasing temperature up to 1300°C. While the flexural strength decreased drastically at 1400°C. The maximum fracture strength at high temperature depends on both chemical composition and the amount of grain boundary glassy phase. The increase in strength and fracture toughness for the SiO2-rich specimens at high temperatures is explained in terms of stress relaxation and/or crack healing in the grain boundary glassy phase, and pull out of acicular mullite grains due to decrease in viscosity of the glassy phase, respectively.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call