Abstract
ZrC/ZrB 2 multilayered coatings with bilayer periods ranging from 4.4 to 35.5 nm were synthesized by r.f. magnetron sputtering. X-ray diffraction, scanning electron microscopy and nanoindention were employed to investigate the microstructure and mechanical properties of the nanoscale multilayers. The results indicated that all coatings had the clear multilayered structure with mixed ZrB 2(0 0 1), ZrB 2(0 0 2) and ZrC(1 1 1) preferred orientations. The maximum hardness (41.7 GPa) was observed in the multilayer with 27.5-nm thick period, which is about 25% higher than the rule-of-mixture value of the monolithic ZrC and ZrB 2 coatings. It also exhibited the best adhesion. Its critical load was over 70 mN. While through insert ZrB 2 into ZrC layer periodically, higher residual stress built in ZrC layer can be released.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.