Influence of Al on the fatigue crack growth behavior of Fe–22Mn–(3Al)–0.6C TWIP steels

Abstract

The influence of Al on fatigue crack growth (FCG) behavior of the high-Mn austenitic twinning-induced plasticity (TWIP) steel was investigated by conducting FCG tests on Fe–22Mn–0Al–0.6C and Fe–22Mn–3Al–0.6C TWIP steels (hereafter, referred to as 0Al and 3Al TWIP steel, respectively). The FCG tests were performed at stress ratio of 0.1 under the control of stress intensity factor range using three-point bending specimens. Excepting that the traditional two-dimensional (2D) observation methods (optical, scanning and transmission electron microscopes) were used to observe the crack paths, fracture surfaces and microstructure features, a high-resolution synchrotron X-ray computed tomography was also applied to observe the three-dimensional (3-D) crack morphology. The results indicate that the FCG resistance of the 0Al TWIP steel is superior to that of 3Al TWIP steel in the near threshold regime. Observed from the 2D crack paths and 3D crack morphologies, it can be found that the crack surface roughness and crack deflection of the 0Al steel are greater than those of 3Al steel. It is suggested that the degree of roughness-induced crack closure decreases with the addition of Al. And the 0Al steel shows much larger plastic zone sizes ahead of the crack tip than the 3Al steel, suggesting that plasticity-induced crack closure may also play an important role in decreasing the FCG rate in the 0Al steel. By excluding the crack closure effects, the 0Al steel still exhibits a higher effective crack growth threshold value than the 3Al steel; this is considered to be due to the higher planarity of slip in the 0Al steel than in the 3Al steel, and the mechanical twins generated in the 0Al steel reduce the stress concentration at crack tip.