Abstract
Viscosity, density, and the undercooling ability of the Zr-based bulk glass forming melt, which was manufactured in two different degrees of purity, have been studied. Investigations have been carried out by means of Couette rheometry and electrostatic and electromagnetic levitation with the latter under microgravity conditions. We found that oxygen and impurities present in industrial grade metals do not significantly alter the melt viscosity and density, while they clearly affect the undercooling ability. Comparing container based and containerless results showed that Couette rheometry can be applied in the temperature range between 1150 K and 1375 K, where it provides reliable data, but only at a rather low oxygen content. Higher oxygen contents, as in the case of the industrial grade alloy, cause measurement artefacts. In the case of Zr59.3Cu28.8Al10.4Nb1.5 alloys, these findings allow a better localization of the key factors dominating the glass forming ability.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.