Abstract

Inductive preheating is well known as possibility to heat ferromagnetic materials. In brazing preheating causes an improvement of wetting quality, e.g. smaller wetting angles and longer wetting lengths. In this paper inductive preheating is used to support a laser beam hybrid joining process. Aluminum AA6016 is molten in order to wet the surface of AlSi- coated steel 22MnB5. Investigations on the influence of preheating on wetting characteristics and intermetallic phase seam formation were carried out. Strength values up to 230 MPa have been measured in tensile shear tests. Fraction zone occurs in the aluminum base material indicating uncritical thickness of the intermetallic phase seam at the interface.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.