Abstract
High-density WC-FeNi ceramic-metal (cermet) composites were fabricated using liquid-phase spark plasma sintering/field-assisted sintering technology (SPS/FAST) with in-situ formation of metal binder phase. The precursor materials were micron-sized powders of WC, Fe, Ni, and C. A low melting point from a eutectic reaction of the powders enabled the in-situ formation of FeNi alloy and facilitates liquid-phase sintering of the WC. The carbon powder was added to stabilize the formation of the binder phase. Electron backscatter diffraction (EBSD) was performed to measure grain size and orientation. The composite exhibited a 99% theoretical density and a microstructure consisting of rounded and contiguous WC grains. The average grain size is 10.5 μm. The composite has a maximum hardness of 16.1 GPa. This research provides a fast and cost-effective approach to fabricate hard metals.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Refractory Metals and Hard Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.