Abstract
Graphene oxide (GO) and nanohydroxyapatite (nHA) are usually used for improving the strength and bioactivity of polymer scaffolds. However, due to the nano-aggregation effect, these applications often face the problems of uneven dispersion and poor interface bonding. In this work, their hybrids (GO@nHA) were constructed by combining chemical modification and in situ growth methods, realizing the perfect combination of nHA and GO. First, the functionalization of GO was realized through oxidative self-polymerization of dopamine (DA), and the product was denoted GO@DA. Furthermore, the in situ growth of nHA on GO@DA was induced by hydrothermal reactions to prepare GO@nHA hybrids. Then, the obtained hybrid was added to the polymer matrix, and a composite scaffold was prepared through a selective laser sintering process. The results demonstrated that with the addition of GO@DA and GO@nHA, the ultimate strength was increased to 16.8 and 18.6 MPa, respectively, which is 66 and 84% higher than the 10.1 MPa of the polylactic acid (PLA) scaffold. In addition, composite scaffolds exhibited good biomineralization ability in vitro and also promoted the adhesion and proliferation of MG63 cells.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.