Abstract
Oxidizing ammonia to nitrogen is a challenge in wastewater treatment. For this challenge ammonia oxidation via chlorine oxide radicals has been proved to be a potential method. In this study, a space-confined photoanode was designed and prepared by loading RuO2 nanoparticles on TiO2/WO3 nanowires for in situ enhancing the generation of chlorine oxide radical. Scanning electron microscopy characterization confirmed that RuO2 nanoparticles were uniformly deposited on TiO2/WO3 nanowires. The generation of chlorine oxide radical was markedly boosted, and its steady-state concentration reached 2.76 × 10−12 M. This value was 3 times that of the traditional bifacial electrode (a type of electrode that has been widely used for chlorine oxide radical-related research). As a result, ammonia oxidation was greatly enhanced. In 90 min, 31.9 mg/L ammonia nitrogen could be degraded, yet only 0.94 mg/L nitrate was accumulated. In addition, the space-confined photoanode exhibited good performance for real wastewater treatment, and 41.0 mg/L ammonia nitrogen could be oxidized in 135 min. During photoelectrocatalysis, a synergistic index (47.7 %) was obtained. Besides the synergistic effect between photocatalysis and electrocatalysis, the unique morphology and structural design (TiO2/WO3 and RuO2 were mainly responsible to hydroxyl radical generation and free chlorine production, respectively) also synergistically promoted the generation of chlorine oxide radical, thereby improving ammonia oxidation. The mechanism for ammonia oxidation via chlorine oxide radicals over the space-confined photoanode was proposed based on experimental results and theoretical calculations.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call