Abstract
Electrodeposition and electropolishing of nanograined nickel has been observed using an in situ electrochemical wet cell developed for transmission electron microscopy. The cell employs two thin film nickel electrodes in a 0.1 M aqueous NiCl 2 electrolyte, which were biased at ±1 V. Anisotropic electrodeposition was observed in which growth of the nickel film across the substrate occurred much more rapidly than growth perpendicular to the substrate. The anisotropic behavior results from relatively equiaxed nanograins nucleating at the growth front with little subsequent coarsening. Grains were observed to nucleate ahead of the growth front, suggesting a new mechanism for electrochemically driven growth across a substrate which depends on ionic surface adsorption ahead of the growth front. During electropolishing the dissolution of nickel tended to occur more isotropically. The film thinned relatively uniformly until certain regions displayed Rayleigh instabilities. At this point the film broke up and some regions coarsened rapidly and/or were subject to electromigration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.