Abstract
We have fabricated and investigated InGaAs Esaki tunnel diodes, grown on GaAs or InP substrates, of varied defect densities. The tunnel diodes exhibit the same I-V characteristics in spite of the variation of defect density. Under the simple thermal annealing and forward current stress tests, the change in the valley current was not observed, indicating that defects were not increased. On the other hand, the reduction in the peak current due to the carbon diffusion was observed under both tests. The diffusion was enhanced by the stress current owing to the energy dissipation associated with the nonradiative electron-hole recombination. From the reduction rates of the peak current, we obtained the thermal and current-enhanced carbon diffusion constants in InGaAs, which are independent of defect density. Although thermal diffusion of carbon in InGaAs is comparable with that in GaAs, the current-induced enhancement of diffusion in InGaAs is extremely weaker than that in GaAs. The difference between activation energy of thermal and current-enhanced diffusion is 0.8 eV, which is independent of stress current density and close to InGaAs bandgap energy. This indicates that the current-enhanced diffusion is dominated by the energy dissipation associated with nonradiative band-to-band recombination. This enhancement mechanism well explains that the current-induced enhancement is independent of defect density and extremely weak. We also have found that the current-enhanced diffusion constant is approximately proportional to the square of current density, suggesting that the recombination in the depletion layer dominates the current-enhanced diffusion.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.