Abstract
In this research, we studied the functional properties of CuCrO2, which is the most promising p-type transparent conductive oxide (TCO). The thin films were fabricated using a spin coating technique. The diffraction patterns were obtained with the help of X-ray diffractions, and the optical properties of absorption characteristics were studied using UV-visible absorption. The physical properties of film formation and surface morphology were analyzed using FESEM analysis. The aging properties were also analyzed with the help of various precursors with different aging times. The CuCrO2 thin films' functional properties were determined by using chelating agent and precursor solution aging times. The CuCrO2 thin films have better transmittance, resistance, figure of merit (FOM), and electrical conductivity. Moreover, the resistivity values of the CuCrO2 thin films are 7.01, 9.90, 12.54, 4.10, 2.42, and 0.35 Ω cm. The current research article covers the preparation of copper chromium delafossite thin films. These thin films can be suitable for hole transport layers in transparent optoelectronic devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.