Abstract
In this study, a compact cold sprayed (CS) Ti coating was deposited on Mg alloy using a high pressure cold spray (HPCS) system. The wear and corrosion behavior of the CS Ti coating was compared with that of CS Al coating and bare Mg alloy. The Ti coating yielded lower wear rate compared to Al coating and Mg alloy. Electrochemical impedance spectroscopy (EIS) and cyclic potentiodynamic polarization (CPP) tests revealed that CS Ti coating can substantially reduce corrosion rate of AZ31B in chloride containing solutions compared to CS Al coating. Interestingly, Ti-coated Mg alloy demonstrated negative hysteresis loop, depicting repassivation of pits, in contrast to AZ31B and Al-coated AZ31B with positive hysteresis loops where corrosion potential (Ecorr) > repassivation potential (Erp); indicating irreversible growth of pits. AZ31B and Al-coated AZ31B were most susceptible to pitting corrosion, while Ti-coated Mg alloy indicated noticeable resistance to pitting in 3.5 wt % NaCl solution. In comparison to Al coating, Ti coating considerably separated the AZ31BMg alloy surface from the corrosive electrolyte during long term immersion test for 11 days.
Highlights
Magnesium (Mg) and its alloys have become a hot topic of research because of the potential engineering applications
Various conversion coatings [1], anodization process, plasma electrolytic oxidation (PEO), physical vapor deposition (PVD), electro-less, before processes: annealing processes, electroplating and ions implantation methods and thermal spray processes have been employed to modify the surface of Mg alloys for improving their wear and corrosion resistances [2,3,4,5,6,7,8,9,10]
AZ31B coated with Ti coating showed the much better corrosion resistance than
Summary
Magnesium (Mg) and its alloys (with a low density of about 1.8 g/cm3 ) have become a hot topic of research because of the potential engineering applications. The inferior wear and corrosion performances of Mg alloys severely limit their extensive applications. The most commonly employed method for improving the surface properties of a substrate is surface treatment In this regard, various conversion coatings [1], anodization process, plasma electrolytic oxidation (PEO), physical vapor deposition (PVD), electro-less, before processes: annealing processes, electroplating and ions implantation methods and thermal spray processes have been employed to modify the surface of Mg alloys for improving their wear and corrosion resistances [2,3,4,5,6,7,8,9,10]
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.