Abstract
We have been investigating the effect of (CoFe2O4)x and (ZnFe2O4)x (x is the wt%) nano-sized ferrites on the superconducting (SC) properties of the high-Tc SC compound GdBa2Cu3O7-δ (Gd123) prepared by the conventional solid-state reaction technique. In this work, the magnetic hysteresis for pure Gd123 samples and samples added with nano-sized ferrites was measured using a superconducting quantum interference device (SQUID) magnetometer using a dc field up to 30,000 Oe. The magnetic Jc was estimated using the extended Bean model. While a clear increase in Jc values with the addition of (CoFe2O4)x nano-sized ferrites is observed, a less clear positive effect on the Jc values is observed with the addition of (ZnFe2O4)x nano-sized ferrites. These results indicate an improvement of grain connectivity, decrease of voids between the grains, and decrease of porosity in Gd123 compound resulting from CoFe2O4 addition consistent with the mechanical properties measured before. (CoFe2O4)x nano-sized ferrite addition has thus resulted in an improvement in the SC properties of Gd123 high-Tc SC compound making it more convenient for applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.