Abstract
The microstructure and mechanical properties of resistance spot welded DP 600 advanced high strength steel and A5052 aluminum alloy joint were improved with 50μm Zn slice interlayer. The results showed that the fusion zone (FZ) grain of A5052 was columnar crystal with rough pattern. The microstructure of FZ and the heat affected zone (HAZ) for DP 600 were coarse-lath martensite and ferrite-fine martensite, respectively. The intermetallic compound (IMC) in the interface region included Fe2Al5, Fe4Al13 and Fe11Zn40. The main IMC was present in winding pattern, which could be responsible for the improvement of mechanical properties. The tensile-shear load reached to a maximum value (7.06kN), increased by 28% as compared to the case without Zn slice interlayer. The obvious plastic deformation took place prior to fracture, and the fracture exhibited plug failure (PF) mode rather than interfacial failure (IF) mode. Many dimples were found on the fracture surface.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call