Abstract
This study aimed to improve Ti-porcelain bonding strength through SiO2 modifications. Wax patterns were coated with SiO2 mixed with tetraethoxy silane (group C), patterns without coating were used as controls and subdivided into sandblasting group (group S) and polishing group (group P). Castingsurfaces were analyzed with XRD, while Ti-ceramic interfaces were characterized using SEM/EDS. Metal-ceramic specimens were tested in three point bending, and characterizations were also analyzed with SEM/EDS of porcelain debonding surfaces. In group C, SiO2 and Ti5Si3 phases were observed; SEM micrograph showed that Ti-porcelain had a compacted interface, and EDS maps of the interface illustrated the diffusion of Si, Al, and Sn to Ti, and cohesive fracture within the bonding agent. The bond strength of group C was 39.04±5.0 MPa, which was 15% higher than that of group S and 32% higher than that of group P. SiO2 coating could improve Ti-porcelain bond strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.