Abstract
This article reports that the enhanced forward gate bias time-dependent dielectric breakdown (TDDB) reliability and interface quality are achieved in 5-nm ferroelectric Hf0.5Zr0.5O2 (HZO) technologies by using the NH3 plasma interfacial layer (IL) treatment and microwave annealing (MWA). An orthorhombic crystalline phase is observed in the annealed HZO film with NH3 plasma IL treatment and MWA, and NH3 plasma IL treatment can suppress Hf/Zr interdiffusion. Metal-oxide-semiconductor capacitors (MOSCAPs) subjected to NH3 plasma IL treatment and 2100-W MWA also have a higher extrapolated operating voltage for a ten-year lifetime at 0.01% failure and lower interface state density ( ${D}_{\textit {it}}$ ) compared to the devices subjected to only rapid thermal annealing (RTA) at 600 °C. Therefore, NH3 plasma treatment and MWA are effective for improving the TDDB reliability and interface quality of the ultrathin ferroelectric HZO.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.