Abstract
ABSTRACTBacterial nanocellulose (BNC) was used to synthesize polyurethane foams (PUFs) prepared from castor oil polyol and MDI diisocyanate using water as the blowing agent. The BNC reacted with the isocyanate, increasing the weight content of urethane hard segments (HS). It did not behave as a nucleation agent, forming a nanometric distribution of cells within the struts followed by a reduction of the apparent density (−7.6%) and a relevant increase of cell size in the growth direction (+37.9%). An alignment of the BNC parallel to the cell walls was observed, producing a nanocomposite with a higher reinforcement weight fraction in that area. At only 0.2 wt %, the BNC behaved as a nanostructured reinforcement, improving the specific compression modulus and strength by +4.67% and +23.6%, respectively, as well as the thermomechanical properties, with an improvement of the specific E′ at 30 °C of +52.4%. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 44982.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.