Abstract
Incorporation of a fourth constituent into CrAlN coating to optimize its properties attracts great attention. Here, the effect of Si on the structure and properties of CrAlN coating is investigated. The solid solution of Si into CrAlN coatings promotes the w-AlN growth, and thus results in a structural transition from Cr0.48Al0.52N with single phase cubic structure to Cr0.42Al0.49Si0.09N and Cr0.37Al0.54Si0.09N with mixed cubic-wurtzite structure. An increase in hardness from ∼25.6 GPa for Cr0.48Al0.52N–∼34.4 GPa for Cr0.42Al0.49Si0.09N and ∼32.7 GPa for Cr0.37Al0.54Si0.09N is obtained due to the solution hardening and grain refinement. Annealing of Cr0.48Al0.52N leads to c-Cr formation via h-Cr2N under N2 releases as well as w-AlN precipitation. Alloying with Si retards the w-AlN precipitation and N-loss, where the final precipitation phases after annealing of the Si-containing coatings are w-AlN, c-Cr3Si and c-Cr, respectively. Furthermore, the oxidation resistance of CrAlN coating is also improved by Si-addition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.