Abstract
Abstract. In this article, the effect of nano-clay particles and heat-treating on thermo-mechanical fatigue (TMF) behaviors and failures of piston aluminum-silicon (AlSi) alloys was investigated. For this purpose, thermo-mechanical fatigue tests were conducted under out-of-phase (OP) loading conditions. Two loading conditions were checked based on different maximum temperatures (250, 300, and 350 °C) and various thermo-mechanical loading factors (100, 125, and 150%). The minimum temperature was constant in all tests at 50 °C under a heating/cooling rate of 10 °C/s and a dwell time of 5 s. Results showed that the nano-composites had a longer fatigue lifetime, at least 2 times higher, compared to the Al alloy, when the maximum temperature was 250 °C and the thermo-mechanical loading factor was 100%. However, no effective change was seen for the stress value and the plastic strain. At higher maximum temperatures, the change in the material behavior was lower. The fracture analysis by scanning electron microscopy (SEM) demonstrated that both materials had a brittle behavior due to cleavage and quasi-cleavage marks. The damage mechanism was also due to the Si-rich phase and intermetallics, respectively for the crack propagation and the micro-crack initiation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.