Abstract
Magnetron sputtering was used for producing titanium vanadium nitride (TiVN) coatings on brass substrates. In this research, we investigate how changing the sputtering power and nitrogen:argon (N2:Ar) gas ratio affects the structural and tribological properties of TiVN coatings. A scanning electron microscope (SEM) was used to examine TiVN coating surface morphology. Both variants showed a gradual increase in the intensity of the TiVN coatings' (111) and (222) peaks. The TiVN coatings' tribological properties were examined using a pin-on-disc tribometer with varying loads, speeds, and sliding distances. The wear rates of TiVN-coated brass pins were in the range of 2.5 × 10-4 to 9.14 × 10-4 mm3/Nm depending on load, sliding distance, and gas ratio variation, when compared to the wear rates of TiVN-coated brass pins deposited at various powers, which ranged from 1.76 × 10-3 to 5.87 × 10-3 mm3/Nm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.