Abstract
This paper reports on electrophoretic deposition of hydroxyapatite coatings on 316L stainless steel and Ti6Al4V alloy. Coatings were carried out at 60 sec. deposition time and voltage values of 40, 80, 120, 160 Voltage. Suspension: It was prepared by using Ethanol, Hydroxyapatite, Polyvinyl Alcohol, Sodium dodecyl sulfate, N-N-Dimethylformamide chemicals. The findings and results acquired at the end of the study have been presented and discussed. When the Ca/P values calculated in the study are examined, it was seen that there are values close to the ideal Ca/P ratio (1.67) in all parameters. When the roughness values are examined, it was seen that coatings close to the ideal surface roughness value (1-1.5 µm) are obtained. When the nano indentation test results were evaluated, it was observed that coatings suitable for shell bone implants were obtained.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Advanced Researches and Engineering Journal
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.