Abstract
ObjectivesTo characterize the optical and mechanical properties of a commercial and in-house translucent Y-TZP before and after aging in autoclave or hydrothermal reactor. MethodsIn-house experimental discs were obtained through uniaxial and isostatic pressing a translucent Y-TZP powder and sintering at 1,550 °C/1 h. Commercial discs were milled from pre-sintered blocks fabricated with the same powder through uniaxial and isostatic pressing and sintering. Discs were allocated into three groups according to aging condition: immediate, aged via autoclave, or reactor (134 °C, 20 h, 2.2 bar). Crystalline content and microstructure were evaluated using X-ray diffraction (XRD) and scanning electron microscopy (SEM). Residual compressive stress (CS) was determined by Raman spectroscopy. Optical properties were determined by the contrast ratio (CR) and translucency parameter (TP) using reflectance data. Mechanical properties were assessed by Vickers hardness, fracture toughness and biaxial flexural strength tests. ResultsXRD and SEM revealed a typical Y-TZP crystalline content, chiefly tetragonal phase, and a dense crystalline matrix for both processing protocols. Reactor aging triggered a more pronounced t-m transformation relative to autoclave. In-house and commercial Y-TZPs demonstrated similar CR and TP, with reactor aging significantly increasing their translucency. Similarly, reactor aging influenced Vickers hardness and fracture toughness. In-house processed Y-TZP clearly demonstrated the presence of CS, whereas commercial Y-TZP showed no presence of CS. Non-aged in-house Y-TZP resulted in significantly lower characteristic strength relative to commercial Y-TZP. While aging protocols significantly increased the characteristic strength of in-house Y-TZP, reactor significantly decreased commercial Y-TZP characteristic strength. Both Y-TZP processing protocols demonstrated high reliability at high-stress missions, with no detrimental effect of aging. ConclusionsLaboratory aging methodology significantly influenced optical and mechanical properties of a commercial and in-house translucent Y-TZP.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.