Abstract
ABSTRACTIn the current work, carbon materials were used in the hydrogen adsorption process, specifically as carbons doped with platinum dispersed on ceria. The textural characterization results of the prepared samples and the starting carbon showed the presence of both micro‐ and mesopores. On the other hand, it has been observed that the specific areas were inversely proportional to the CeO2 loading. In addition, the amount of adsorbed hydrogen increased after doping the carbon with platinum and, even more, when the carbon was doped with Pt dispersed on ceria (2.2 mg/g at 25°C and 30 bar). However, there was a ceria optimum from which the adsorption capacity decreased (10% wt). The results of temperature‐programmed desorption (TPD) of hydrogen indicated a high affinity between Pt and H2 that enhanced H2 adsorption process by establishing chemical bonds between the metal particles and H2. Precisely, the presence of metallic Pt particles dispersed on ceria considerably promotes the spillover process of hydrogen on carbon. This can be confirmed by hydrogen adsorption–desorption isotherms, that showed that complete desorption of chemisorbed hydrogen required an increase of temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.