Hydride VPE: the unexpected process for the fast growth of GaAs and GaN nanowires with record aspect ratio and polytypism-free crystalline structure

Abstract

Hydride Vapor Phase Epitaxy (HVPE) makes use of chloride III-Cl and hydride V-H3 gaseous growth precursors. It is known as a near-equilibrium process, providing the widest range of growth rates from 1 to more than 100 μm/h. When it comes to metal catalyst-assisted VLS (vapor-liquid-solid) growth, the physics of HVPE growth is maintained: high dechlorination frequency, high axial growth rate of nanowires (NWs) up to 170 μm/h. The remarkable features of NWs grown by HVPE are the untapered morphology with constant diameter and the stacking fault-free crystalline phase. Record pure zinc blende cubic phase for 20 μm long GaAs NWs with radii of 10 and 5 nm is shown. The absence of wurtzite phase in GaAs NWs grown by HVPE whatever the diameter is discussed with respect to surface energetic grounds and kinetics. Ni assisted, Ni-Au assisted and catalyst-free HVPE growth of wurtzite GaN NWs is also addressed. Micro-photoluminescence spectroscopy analysis revealed GaN nanowires of great optical quality, with a FWHM of 1 meV at 10 K for the neutral donor bound exciton transition.