Abstract
The grain stresses within hydrides precipitated in rolled zircaloy-4 plates were determined by synchrotron X-ray diffraction experiments using an 80 keV photon beam and a high-speed area detector placed in transmission geometry. Results showed large compressive stresses (360 ± 20 MPa) in the hydrides along the plate rolling direction. The origin of these stresses was investigated by performing hydride dissolution/precipitation in situ for thermal cycles between room temperature and 400 °C. A large stress hysteresis was observed, with a steady decrease on heating and an abrupt change on cooling. The observed stresses are explained by the constraint imposed by grain boundaries on the growth of hydride platelets on the rolling–transverse plane of the rolled plates.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.