Abstract
SiC ceramics with 0.5 wt% B4C and 0.5 wt% C as sintering additives were prepared by hot oscillatory pressure (HOP) and hot pressure (HP). The mechanical properties and microstructures of the resultant ceramics were investigated. The results showed that the oscillatory pressure could effectively suppress the abnormal growth of SiC grains and promote the formation of high-density dislocation and stacking faults. The hardness of SiC ceramics made by HOP at 2000oC reached 28.9 GPa, which was much higher than that (25.9 GPa) of the sample made by HP at the same temperature. The current study suggests that HOP is a promising technique for preparing high-performance SiC ceramics.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.