Abstract
ABSTRACTHot cracking susceptibility of the Fe–Ni-based precipitation hardening cast superalloy Alloy 718 was studied by Varestraint weldability testing. The effect of two hot isostatic pressing (HIP) treatments commonly employed in the aerospace industry was investigated in reference to the as cast condition. It was found that the heat affected zone (HAZ) liquation cracking susceptibility increased for samples with pre-weld HIP treatments. The as cast condition disclosed the best response for liquation cracking followed by HIP-1120 (1120°C/4h (HIP) + 1050°C/1h and furnace cooling to 650°C/1h in vacuum + 950°C/1h) and HIP-1190 (1190°C/4h (HIP) + 870°C/10h and furnace cooling to 650°C/1h in vacuum + 950°C/1h). The amount of the secondary precipitates and base metal grain size was found to be important parameters influencing the cracking susceptibility. Regarding solidification cracking susceptibility, the three conditions appear to behave similarly.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.