Abstract
The homogenization of AlSi7MgCu0.5 alloy as-cast structure by using an equal channel angular pressing (ECAP) was investigated. The heat treatment of as-cast alloy applied before ECAP processing was required to increase alloy plasticity. Therefore, the samples of analyzed alloy were solution annealed at temperature of 550 °C for 4 hours and subsequently water quenched. Quenched samples were artificially aged at temperature of 300 °C for 5 hours to obtain an over-aged alloy state. The solution annealing of as-cast alloy state caused a partial spheroidization and coarsening of eutectic Si-particles. During artificial aging of analyzed alloy, the incoherent particles precipitated uniformly from α-solid solution. The ECAP technique at room temperature homogenized its heterogeneous dendritic microstructure and formed the ultra-fine grains of solid solution. A redistribution and fragmentation of the eutectic Si-particles and precipitated particles was occurred.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.