Homoepitaxial growth of β-Ga2O3 layers by halide vapor phase epitaxy

Abstract

Thick high-purity β-Ga2O3 layers of high crystalline quality were grown homoepitaxially by halide vapor phase epitaxy (HVPE) using gaseous GaCl and O2 on (001) β-Ga2O3 substrates prepared by edge-defined film-fed growth. The surface morphology and structural quality of the grown layer improved with increasing growth temperature. X-ray diffraction ω-rocking curves for the (002) and (400) reflections for the layer grown at 1000 °C had small full widths at half maximum. Secondary ion mass spectrometry and electrical characteristics revealed that the growth of high-purity β-Ga2O3 layers with low effective donor concentration (Nd − Na < 1013 cm−3) is possible by HVPE.