Abstract
This study presents the development of a highly robust, pressureless, and void-free silver sinter-bonding technology for power semiconductor packaging. A bimodal silver paste containing silver nanoparticles and sub-micron particles was used, with polymethyl methacrylate (PMMA) as an additive to provide additional thermal energy during sintering. This enabled rapid sintering and the formation of a dense, void-free bonding joint. The effects of sintering temperature and PMMA content on shear strength and microstructure were systematically investigated. The results showed that the shear strength increased with rising sintering temperatures, achieving a maximum of 41 MPa at 300 °C, with minimal void formation due to enhanced particle necking facilitated by PMMA combustion. However, at 350 °C, the shear strength decreased to 35 MPa due to cracks and voids at the copper substrate–copper oxide interface caused by thermal expansion mismatch. The optimal PMMA content was found to be 5 wt.%, balancing sufficient thermal energy and void reduction. This pressureless sintering technology demonstrates significant potential for high-reliability applications in power semiconductor modules operating under high-temperature and high-stress conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.