Abstract
In this study, SnO2-based varistors were prepared from mechanically activated nanocrystalline powders. Nanocrystalline powders were derived by subjecting the initial powders to intensive high-energy activation with different times and ball to powder ratio. The effect of activation parameters on the powder properties and sintering temperature, as well as microstructural, micro-electrical and macro-electrical properties of the final specimens was evaluated. Varistors derived from high-energy mechanical activation exhibit a higher density (98.3% relative density) and more refined microstructure upon sintering at 1,300 °C in comparison varistors prepared from conventional powders. Breakdown voltage and nonlinear coefficient were increased up to 24 kV/cm and 45 respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.