Abstract
Mn/Y codoped Ba0.67Sr0.33TiO3 (BST) ceramics were fabricated via using citrate–nitrate combustion derived powder, and the effect of sintering temperature on microstructure and electrical properties of BST ceramics were mainly investigated. Agglomerated BST powder, with nano-size particles, was obtained at 700°C. Sintering temperature has a strong influence on the microstructure and electrical properties of BST ceramics. The density, dielectric and ferroelectric properties are improved by optimizing sintering temperature. The relative density of the BST ceramics sintered at an optimum sintering temperature (1260°C) reaches 97.9% of the theoretical value. The measured values of remanent polarization (2Pr) and coercive field (2Ec) of the BST ceramics are 16.33μC/cm2 and 3.548kV/cm, respectively. The dielectric loss of the BST ceramics is 0.003 in the para-electric state. Therefore, nanocrystalline powder, sintering with optimum temperature and Mn/Y codoping help improve the electrical properties of BST ceramics.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.