Abstract
The simulated fine grained heat-affected zone (FGHAZ) specimens for P92 welded joints were prepared by heat treatment, then the creep tests were carried out at 650 °C under the applied stress of 90–120 MPa to investigate high-temperature creep behavior of FGHAZ. The results show that the creep property of FGHAZ is much inferior to that of the base metal, which exhibits the much higher steady creep rate and shorter time to creep fracture. The power law equation can describe the steady creep rate dependence on applied stress, indicating that the stress exponent n of FGHAZ is distinguished between two regions with n=15.1 at high stresses (more than 100 MPa) and n=8.64 at lower stresses. Based on Monkman-Grant equation, the relationship between the secondary creep rate and time to rupture is obtained to evaluate the creep life of FGHAZ with the applied stress above 100 MPa.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.