Abstract
Several Nb based alloys (Nb-20Mo-15Si-25Cr, Nb-20Mo-15Si-25Cr-5B, Nb-20Si-20Cr-5Al, and Nb-20Cr-20Si-5Hf) have been prepared to evaluate the oxidation resistance from 700 to 1400°C in air. The phase identification was determined by calculating the isothermal sections in this temperature range using PANDATTM software. The experiments involve static heating for 24 hours (short term oxidation, STO) or 7 cycles of 24 hour heating (long term oxidation, LTO). Weight gain per unit area as a function of either temperature (STO) or time (LTO) has been used to determine their oxidation resistance. However, SEM, EDS on SEM, x-ray mapping, and XRD have been used to evaluate the oxide scale characterization and the influence of various microconstituent effects have been determined. It appears that B addition may be beneficial while Al is advantageous in comparison to Hf addition. The problem of pesting, typically, in a range of temperature from 900 to 1100°C needs to be controlled through minor additions since the alloys exhibit fairly good resistance at lower and higher temperatures up to 1400°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.