Abstract
Due to the efficient photocarrier separation and collection coming from their distinctive band structures, superlattice nanowires (NWs) have great potential as active materials for high-performance optoelectronic devices. In this work, InGaZnO NWs with superlattice structure and controllable stoichiometry are obtained by ambient-pressure chemical vapor deposition. Along the NW axial direction, perfect alternately stacking of InGaO(ZnO)4+ blocks and InO2- layers is observed to form a periodic layered structure. Strikingly, when configured into individual NW photodetectors, the Ga concentration is found to significantly influence the amount of oxygen vacancies and oxygen molecules adsorbed on the NW surface, which dictate the photoconducting properties of the NW channels. Based on the optimized Ga concentration (i.e., In1.8Ga1.8Zn2.4O7), the individual NW device exhibits an excellent responsivity of 1.95 × 105 A/W and external quantum efficiency of as high as 9.28 × 107% together with a rise time of 0.93 s and a decay time of 0.2 s for the ultraviolet (UV) photodetection. Besides, the obtained NWs can be fabricated into large-scale parallel arrays on glass substrates as well to achieve fully transparent UV photodetectors, where the performance is on the same level or even better than many transparent photodetectors with high performance. All the results discussed above demonstrate the great potential of InGaZnO superlattice NWs for next-generation advanced optoelectronic devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.