Abstract
Silica nanosheets (SN) derived from natural vermiculite (Verm) were successfully incorporated into polyethersulfone–polyvinylpyrrolidone (PES–PVP) polymer to fabricate high–temperature proton exchange membranes (HT–PEMs). The content of SN filler was varied (0.1–0.75 wt%) to study its influence on proton conductivity, power density and durability. Benefiting from the hydroxyl groups of SN that enable the formation of additional proton–transferring pathways, the inorganic–organic membrane displayed enhanced proton conductivity of 48.2 mS/cm and power density of 495 mW/cm2 at 150 °C without humidification when the content of SN is 0.25 wt%. Furthermore, exfoliated SN (E–SN) and sulfonated SN (S–SN), which were fabricated by a liquid–phase exfoliation method and silane condensation, respectively, were embedded in PES–PVP polymer matrix by a simple blending method. Due to the significant contribution from sulfonic groups in S–SN, the membrane with 0.25 wt% S–SN reached the highest proton conductivity of 51.5 mS/cm and peak power density of 546 mW/cm2 at 150 °C, 48% higher than the pristine PES–PVP membranes. Compared to unaltered PES–PVP membrane, SN added hybrid composite membrane demonstrated excellent durability for the fuel cell at 150 °C. Using a facile method to prepare 2D SN from natural clay minerals, the strategy of exfoliation and functionalization of SN can be potentially used in the production of HT–PEMs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.