High-Performance Metal–Insulator–Metal Capacitors Using Europium Oxide as Dielectric

Abstract

We report the first demonstration of metal-insulator-metal (MIM) capacitors with Eu <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> dielectric for analog and DRAM applications. The influence of different anneal conditions on the electrical characteristics of the fabricated MIM capacitors is studied. FG anneal results in high capacitance density (7 fF/μm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> ), whereas oxygen anneal results in low quadratic voltage coefficient of capacitance (VCC) (194 ppm/V <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> at 100 kHz), and argon anneal results in low leakage current density (3.2 ×10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-8</sup> A/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> at -1 V). We correlate these electrical results with the surface chemical states of the films through X-ray photoelectron spectroscopy measurements. In particular, FG anneal and argon anneal result in sub-oxides, which modulate the electrical properties.