Abstract
Steady state (1973K, 180s) and repeated (723K–1524K, 380times) heat loading experiments of ITER grade W and toughened, fine-grained, recrystallized W–1.1TiC (TFGR W–1.1TiC) have been performed using an electron beam irradiation system. In ITER grade W, the irradiation around 1973K causes recrystallization and grain growth up to the average diameters of 50–100μm. Repeated irradiations cause significant surface roughening, cracking at grain boundaries and surface exfoliation. On the other hand, TFGR W–1.1TiC does not exhibit any surface roughening or cracking after repeated heat loading although grain boundaries on the surface of TFGR W–1.1TiC can be observed after irradiation at around 1973K 180s by steady state heat loading.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.