Abstract
The miniaturization and integration trend of electronic applications requires high energy storage performance, and the development of multilayer ceramic capacitors (MLCC) demands the compatibility between ceramic sintering temperature and co-firing temperature of metal electrodes. Herein, we obtained a high recoverable energy storage density and a low sintering temperature simultaneously in 0.5(Bi0.5Na0.5)TiO3-0.5SrTiO3-x mol% CuO (0.5BNT-0.5ST-x mol% CuO) via the combination of adding CuO sintering aid and citrate sol-gel synthesis method. The optimum sintering temperature decreases significantly from 1130 °C for x = 0 to 820 °C for x = 2.0. The ceramic of 0.5BNT-0.5ST-1.5 mol% CuO exhibits a large Wrec of 2.20 J/cm3 and η of 72.39% under 230 kV/cm. Furthermore, the same sample also possesses a large CD of 1740.97 A/cm2, an extremely high PD of 139.28 MW/cm3 and an ultrafast discharge speed of 82 ns. These merits reveal that the ceramic of 0.5BNT-0.5ST-1.5 mol% CuO has great potential in practical MLCC production.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.