Abstract
Our objective in this work is to study the HF etching chemical treatment effect on the mechanical and optical properties of soda-lime glass eroded with 200 g fixed sand mass. We followed the evolution of these properties in relation to the chemical attack duration. The results show a clear improvement of the measured properties. The strength of the eroded samples is 44.23 ± 0.91 MPa. It increases up to 57.73 ± 1.76 MPa after 15 min of treatment and reaches 181.43 ± 23.69 MPa after 1 h. This last value is much higher than the as received glass strength (117.5 ± 10.48 MPa). The optical transmission of the eroded samples is about 18.5%. During the first 2 min of the chemical treatment, an important drop of the optical transmission (12%) was observed. However, improvement of the transmission was achieved for longer chemical treatment durations. After 8 h of treatment, the optical transmission increases up to 57%. Microscopic observations show that the HF attack causes the opening and the blunting of the surface cracks. In general, the surface state is improved during the chemical treatment.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call