Hexagonal (wurtzite) GaN inclusions as a defect in cubic (zinc-blende) GaN

Abstract

The dependence of the hexagonal fraction with thickness in MBE-grown bulk cubic (c-) GaN epilayer is presented in this paper. A number of c-GaN epilayers with different thicknesses were characterized via PL and XRD measurements. From the PL spectra, the signal due to h-GaN inclusions increases as the thickness of the c-GaN increases. On the contrary, in the XRD diffractogram, c-GaN shows a dominant signal at all thicknesses, and only a weak peak at ∼35° is observed in the diffractogram, implying the existence of a small amount of h-GaN in the c-GaN layer. The best quality of c-GaN is observed in the first 10μm of GaN on the top of GaAs substrate. Even though the hexagonal content increases with the thickness, the average content remains below 20% in c-GaN layers up to 50μm thick. The surface morphology of thick c-GaN is also presented.