Abstract
The present work is a contribution in investigating the effect of heat treatment on microstructure, hardness and friction wear of A105N steel. Samples of 25x25 mm2 cross-section and 15mm thickness have been prepared from the as-received material and then heat-treated. The samples were austenitized at 1050°C for 60 minutes followed by water quenching, then tempered at 500 and 700°C for 120 minutes. Microstructural changes and their effect on the wear resistance and hardness were investigated according to the applied heat treatments. The main results show that after quenching the structure is mostly composed of quenched martensite, which confers high hardness and friction resistance to the steel. While the tempered structure is composed of tempered martensite and ferrite. As the temperature rises to 700°C, the tempered martensite decreases and is fully transformed to ferrite and cementite. A good wear resistance expressed by a low friction coefficient and a low wear rate is achieved by tempering at 500°C.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call