AbstractThe unique nonlinear dielectric properties of antiferroelectric (AFE) oxides are promising for advancements in solid state supercapacitor, actuator, and memory technologies. AFE behavior in high‐k ZrO2is of particular technological interest, but the origin of antiferroelectricity in ZrO2remains questionable. The theory of reversible electric field‐induced phase transitions between the nonpolar P42/nmc tetragonal phase and the polarPca21orthorhombic phase is experimentally tested with local structural and electromechanical characterization of AFE ZrO2thin films. Piezoresponse force microscopy identifies signature evidence of a field‐induced phase transition. A significant size effect in AFE ZrO2is experimentally observed as film thickness is scaled down from 14.7 to 4.3 nm. The size effect is explained by modifications to the phase transition energy barrier heights ranging from 0.6 to 7.6 meV f.u−1depending on crystallite size and in‐plane compressive strain with decreasing ZrO2film thickness. Using the size effect, it is possible to double the energy storage density in ZrO2from 20 J cm−3to greater than 40 J cm−3, thus highlighting a feasible route for superior performance in AFE fluorite supercapacitors.
Accepted Version (
Free)
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call