Abstract

Copper indium diselenide (CuInSe 2) compound was synthesized by reacting its constituent’s elements copper, indium and selenium in near stoichiometric proportions (i.e. 1:1:2 with 5% excess selenium) in an evacuated quartz ampoule. Synthesized pulverized compound material was used as an evaporant material to deposit thin films of CuInSe 2 onto organically cleaned sodalime glass substrates, held at different temperatures (300–573 K), by means of single source thermal evaporation method. The phase structure and the composition of chemical constituents present in the synthesized compound and thin films have been investigated using X-ray diffraction and energy dispersive X-ray analysis, respectively. The investigations show that CuInSe 2 thin films grown above 423 K are single phase, having preferred orientation of grains along the (112) direction, and having near stoichiometric composition of elements. The surface morphology of CuInSe 2 films, deposited at different substrate temperatures, has been studied using the atomic force microscopy to estimate its surface roughness. An analysis of the transmission spectra of CuInSe 2 films, recorded in the wavelength range of 500–1500 nm, revealed that the optical absorption coefficient and the energy band gap for CuInSe 2 films, deposited at different substrate temperatures, are ∼10 4 cm −1 and 1.01–1.06 eV, respectively. The transmission spectrum was analyzed using iterative method to calculate the refractive index and the extinction coefficient of CuInSe 2 thin film deposited at 523 K. The Hall effect measurements and the temperature dependence of the electrical conductivity of CuInSe 2 thin films, deposited at different substrate temperatures, revealed that the films had electrical resistivity in the range of 0.15–20 ohm cm, and the activation energy 82–42 meV, both being influenced by the substrate temperature.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call